當(dāng)雙組份膠在混合過(guò)程中就發(fā)生局部固化時(shí)，膠槍打出來(lái)的膠就會(huì)出現(xiàn)結(jié)皮或硫化現(xiàn)象。出現(xiàn)這一現(xiàn)象的原因主要有三種：
When the two-component rubber is partially cured in the mixing process, the rubber produced by the rubber gun will be skinned or vulcanized. There are three main reasons for this phenomenon:
⑴膠體顏色較黑，固化快時(shí)，可能是由于B組分比例過(guò)高，過(guò)多的催化劑促使固化速度加快。此時(shí)，需要適當(dāng)降低B組分的比例，將結(jié)皮或硫化膠沖洗干凈后施工；
⑴ when the colloid color is black and the curing speed is fast, it may be due to the high proportion of component B and too much catalyst to accelerate the curing speed. At this time, it is necessary to properly reduce the proportion of component B and wash the crust or vulcanizate before construction;
⑵若打膠過(guò)程中伴有出膠慢的現(xiàn)象時(shí)，可能是混合芯長(zhǎng)時(shí)間未清洗或清洗不徹底，膠體結(jié)皮堵塞管道。因此，定期清洗靜態(tài)混合器是很有必要的。
(2) if the glue is slowly discharged during the gluing process, the mixing core may not be cleaned for a long time or not completely, and the colloidal crust blocks the pipeline. Therefore, it is necessary to clean the static mixer regularly.

⑶當(dāng)固化和出膠速度均無(wú)異常，而打出的膠仍有結(jié)皮或硫化現(xiàn)象時(shí)，則可能是設(shè)備停機(jī)時(shí)間較長(zhǎng)，膠槍未清洗或洗槍不夠徹底，需要將結(jié)皮或硫化膠沖洗干凈后后施工。
(3) when there is no abnormality in the curing and rubber outlet speed, and the rubber is still crusted or vulcanized, the equipment may be shut down for a long time, the rubber gun is not cleaned or the gun is not cleaned thoroughly, so it is necessary to wash the crusted or vulcanized rubber before construction.
般而言，膠體本身是沒(méi)有氣泡的，膠體夾有的氣泡極可能是運(yùn)輸或施工過(guò)程中混入了空氣，如：⑴更換膠桶時(shí)排氣未排干凈；⑵組分在上機(jī)后壓盤(pán)未壓下去，導(dǎo)致排泡不徹底。 因此，在使用前排泡要徹底，使用過(guò)程中應(yīng)正確操作打膠機(jī)，保證密封從而阻止空氣進(jìn)入。若懷疑產(chǎn)品自身就帶有氣泡，可以通過(guò)蝴蝶試驗(yàn)來(lái)進(jìn)行判斷。頭條萊垍
Generally speaking, the colloid itself has no bubbles, and the bubbles contained in the colloid are likely to be mixed with air during transportation or construction, such as: (1) the exhaust is not discharged completely when replacing the rubber barrel; (2) after the components are put on the machine, the pressure plate is not pressed down, resulting in incomplete bubble discharge. Therefore, the foam should be thoroughly before use. During use, the glue applicator should be operated correctly to ensure sealing, so as to prevent air from entering. If it is suspected that the product itself has bubbles, it can be judged by butterfly test. Headline Lai long